蠕墨铸铁/40Cr配副干摩擦三维表面形貌特征研究[J]. 摩擦学学报, 2000, 20(6): 407-411.
引用本文: 蠕墨铸铁/40Cr配副干摩擦三维表面形貌特征研究[J]. 摩擦学学报, 2000, 20(6): 407-411.
3-D Topographical Characteristics of Dry Sliding Surface of Compacted Graphite Irons Coupled with Chromium Steel Disk[J]. TRIBOLOGY, 2000, 20(6): 407-411.
Citation: 3-D Topographical Characteristics of Dry Sliding Surface of Compacted Graphite Irons Coupled with Chromium Steel Disk[J]. TRIBOLOGY, 2000, 20(6): 407-411.

蠕墨铸铁/40Cr配副干摩擦三维表面形貌特征研究

3-D Topographical Characteristics of Dry Sliding Surface of Compacted Graphite Irons Coupled with Chromium Steel Disk

  • 摘要: 采用探针式三维表面形貌仪考察了销-盘式干磨擦试验条件下蠕墨铸铁度销磨损表面的三维形貌特征。结果表明:度销磨损表面主要呈现犁沟型、孤岛型及二者的混合型3种形貌特征,其中具有孤岛型磨损表面形貌特征的试样的摩擦系数较高,磨损率较低;而具有犁沟型磨损表面形貌特征的试样的摩擦系数最低,磨损率最高,分析表面形貌参数发现:犁沟型表面形貌具有最大的表面高度偏差和表面空隙率及高负值的表面高度分布参数;而孤岛型表面形貌的表面高度偏差和表面空隙率最小,表面高度分布参数为高正值。

     

    Abstract: The topographical characteristics of the worn surfaces of compacted graphite iron (coded as C G iron) in dry sliding against 40Cr steel were investigated with a 3 D surface profilometer. The topographical parameters have been analyzed by taking into account the thermal effect during the friction process. As the results, three kinds of typical topographical features have been observed for the worn surfaces of C G iron with various P content. Namely, C G iron with 0.05% P, 1.30% P, and 0.70% P show worn surfaces characterized by groove ridge, peak pits and their combined topography. The C G iron specimen with peak pits type worn surface topography showes the lowest wear rate and highest friction coefficient, while that with groove ridge type worn surface topography shows the highest wear rate and lowest friction coefficient. The groove ridge type worn surface has a relatively large value of surface height deviation and void volume ratio and negative large value of skewness, which is contrary to the peak pits topography.

     

/