含硼咪唑啉化合物的摩擦学性能研究[J]. 摩擦学学报, 1999, 19(2): 162-165.
引用本文: 含硼咪唑啉化合物的摩擦学性能研究[J]. 摩擦学学报, 1999, 19(2): 162-165.
Study of the Tribological Properties of Imidazoline Borate as Additive in Water[J]. TRIBOLOGY, 1999, 19(2): 162-165.
Citation: Study of the Tribological Properties of Imidazoline Borate as Additive in Water[J]. TRIBOLOGY, 1999, 19(2): 162-165.

含硼咪唑啉化合物的摩擦学性能研究

Study of the Tribological Properties of Imidazoline Borate as Additive in Water

  • 摘要: 利用四球试验机考察了2种含硼咪唑啉化合物在水中的摩擦性能,并用X射线光电子能谱(XPS)研究了磨斑表面边界膜的化学组成,摩擦试验表明,含硼咪啉化合物在水中具有良好的润滑性能和承载能力,表面分析证明,含硼咪唑啉化合物的减摩抗磨作用取决于摩擦化学反应生成的有机咪唑啉,RB(OH)2及部分分解产物的复合膜。

     

    Abstract: The tribological properties of imidazoline borates as additive in water were evaluated using a four ball test machine at different additive concentration and load.The rubbed surfaces were investigated using X ray photoelectron spectroscopy. The tribological test results showed the imidazoline borates have good lubricating performance and load carrying capacity.Imidazoline borates reacted with the metal surface in friction process and produced a complex film composed of organic imidazolines and partially decomposed products which contributed to the good lubrication and antiwear properties.

     

/